Cone 10 Redux

Fire Yellow Redux

From ClayUtah forums.

• Custer Feldspar ..... 50
• EPK ......................... 50
• Dolomite ................. 25
• Whiting ................... 10
• Tin Oxide ................. 5.5
• Bone Ash .................. 8
• Red Iron Oxide ....... 1
• Rutile ........................ 2

single-fired, and the kiln was held at 500f and 1800f each, for one hour. Reduction was started after the 1800f soak and carried out to cone 10/11. The kiln was then slowly cooled of about an hour to 2000f and then shut off.

Each glaze was applied to 4 tiles (in the order they'll appear in the photos):

1. over both Red Iron Oxide and Rutile washes
2. 1/2/3 dip on white stoneware
3. 1/2/3 dip on iron rich stoneware
4. over iron red (Ohata) glaze.

Cone 10 Redux

• Potash Feldspar ......... 50
• Dolomite ................... 20
• EPK ........................... 20
• Bone Ash ................... 10
• Vanadium Pentoxide .... 6
• Rutile ......................... 5

single-fired, and the kiln was held at 500f  and 1800f each, for one hour. Reduction was started after the 1800f soak and carried out to cone 10/11. The kiln was then slowly cooled of about an hour to 2000f and then shut off.

Each glaze was applied to 4 tiles (in the order they'll appear in the photos):

1. over both Red Iron Oxide and Rutile washes
2. 1/2/3 dip on white stoneware
3. 1/2/3 dip on iron rich stoneware
4. over iron red (Ohata) glaze.

Cone 10 Redux

• Potash Feldspar ......... 50
• Dolomite ................... 20
• EPK ........................... 20
• Bone Ash ................... 10
• Vanadium Pentoxide .... 6
• Iron Oxide .................. 3

single-fired, and the kiln was held at 500f  and 1800f each, for one hour. Reduction was started after the 1800f soak and carried out to cone 10/11. The kiln was then slowly cooled of about an hour to 2000f and then shut off.

Each glaze was applied to 4 tiles (in the order they'll appear in the photos):

1. over both Red Iron Oxide and Rutile washes
2. 1/2/3 dip on white stoneware
3. 1/2/3 dip on iron rich stoneware
4. over iron red (Ohata) glaze.

Cone 10 Redux

• Potash Feldspar ......... 50
• Dolomite ................... 20
• EPK ........................... 20
• Bone Ash ................... 10
• Vanadium Pentoxide .... 6

single-fired, and the kiln was held at 500f  and 1800f each, for one hour. Reduction was started after the 1800f soak and carried out to cone 10/11. The kiln was then slowly cooled of about an hour to 2000f and then shut off.

Each glaze was applied to 4 tiles (in the order they'll appear in the photos):

1. over both Red Iron Oxide and Rutile washes
2. 1/2/3 dip on white stoneware
3. 1/2/3 dip on iron rich stoneware
4. over iron red (Ohata) glaze.

Cone 10 Redux

• Potash Feldspar ....... 50
• Dolomite ................. 20
• EPK ........................ 20
• Bone Ash ................ 10
• Rutile ..................... 15
• Tin Oxide ................. 5

single-fired, and the kiln was held at 500f  and 1800f each, for one hour. Reduction was started after the 1800f soak and carried out to cone 10/11. The kiln was then slowly cooled of about an hour to 2000f and then shut off.

Each glaze was applied to 4 tiles (in the order they'll appear in the photos):

1. over both Red Iron Oxide and Rutile washes
2. 1/2/3 dip on white stoneware
3. 1/2/3 dip on iron rich stoneware
4. over iron red (Ohata) glaze.

Cone 10 Redux

• Potash Feldspar ....... 50
• Dolomite ................. 20
• EPK ........................ 20
• Bone Ash ................ 10
• Rutile ..................... 15
• Chrome Oxide .......... 0.25

single-fired, and the kiln was held at 500f  and 1800f each, for one hour. Reduction was started after the 1800f soak and carried out to cone 10/11. The kiln was then slowly cooled of about an hour to 2000f and then shut off.

Each glaze was applied to 4 tiles (in the order they'll appear in the photos):

1. over both Red Iron Oxide and Rutile washes
2. 1/2/3 dip on white stoneware
3. 1/2/3 dip on iron rich stoneware
4. over iron red (Ohata) glaze.

Cone 10 Redux

• Potash Feldspar ....... 50
• Dolomite ................. 20
• EPK ........................ 20
• Bone Ash ................ 10
• Rutile ..................... 15

single-fired, and the kiln was held at 500f  and 1800f each, for one hour. Reduction was started after the 1800f soak and carried out to cone 10/11. The kiln was then slowly cooled of about an hour to 2000f and then shut off.

Each glaze was applied to 4 tiles (in the order they'll appear in the photos):

1. over both Red Iron Oxide and Rutile washes
2. 1/2/3 dip on white stoneware
3. 1/2/3 dip on iron rich stoneware
4. over iron red (Ohata) glaze.